Acid Potassium Chloride Zinc Electroplating Brightener
Zinc chloride as the main salt, is also a conductive salt, it in the plating solution all ionized into chloride ions and zinc ions, ionized zinc ions will be directly on the plating part of the cathode reduction into a coating, can increase the conductivity of the plating solution, its concentration allowed to change in a wide range. It is easy to absorb moisture, easy to dissolve, exothermic phenomenon.
Description
Zinc chloride provides zinc ions. When the content of ZnCl12 is set to the upper limit, the cathode current density can be improved and the deposition rate of the coating can be improved, but the dispersion ability and covering ability become worse. When the content of ZnCl12 is set to the lower limit, the dispersion ability can be improved, the loss of the plating parts taking out liquid and the cost of tank fitting and wastewater treatment can be reduced. When the content of ZnCl12 is too low, the concentration polarization will be large, resulting in low current opening, which will narrow the bright area of the plating, decrease the cathode current density accordingly, slow down the deposition rate, and prone to charring phenomenon in the high current density area of the plating.
Common failures and processing method
|
Problem Description |
Probable cause |
Solutions |
|
Poor brightness |
Lack of brightener Lack of softener Organic impurity pollution |
Brightener supplement Softener supplement Activated carbon filtration |
|
Poor coverage No coating in hole and concave
|
Lack of brightener Lack of softener Low potassium chloride The bath temperature becomes higher Aluminum impurity pollution |
Brightener supplement Softener supplement Potassium chloride supplement Lowering temperature Treat with zinc powder |
|
The bright range is narrow and the coating is easy to burn |
The PH value of the bath increases Lack of zinc Lack of boric acid Lack of softener |
Adjust PH value with dilute hydrochloric acid Zinc chloride supplement Boric acid supplement Softener supplement |
|
The coating has white mist |
Effect of organic impurities Poor cleaning after plating |
Activated carbon filtration Change the cleaning water |
|
The coating blackening after acid dipping |
Iron impurity Copper impurity |
Hydrogen peroxide treatment and filtration Treat with zinc powder |
|
Roller holes appear in the coating |
Lack of softener Iron impurity Excessive current Lower zinc Over loading of work |
Softener supplement Hydrogen peroxide treatment and filtration Lower total current Zinc chloride supplement Reduced loading |
Hot Tags: acid potassium chloride zinc electroplating brightener, China acid potassium chloride zinc electroplating brightener manufacturers, suppliers, factory, HL 95 Potassium Chloride Zinc plating Additives B, Zinc Electroplating Alkaline Zincate Cleaning Agent, acid potassium chloride zinc plating chemical solution additives, Acid Electroplating Additives B, HL 5 A Type Acid Potassium Chloride Zinc Plating Intermediate, HL 93 Potassium Chloride Zinc plating Additives B
Send Inquiry
You Might Also Like
-
Acid Potassium Chloride Zinc Electroplating Brightener
-
Acid Potassium Chloride Zinc Electroplating Brightener
-
Acid Potassium Chloride Zinc Electroplating Brightener
-
Acid Potassium Chloride Zinc Electroplating Brightener
-
Acid Potassium Chloride Zinc Electroplating Brightener
-
Acid Potassium Chloride Zinc Electroplating Brightener