Zinc Plate Intermediate

Our main products are chemical additives, which used in manufacture zinc electroplating bath, for improve the brightness of galvanized layer on metal surface. Acid potassium chloride zinc plating brightener, which used in manufacture zinc electroplating bath, for improve the brightness of galvanized layer on metal surface.

Send Inquiry

Description

HL-5 Potassium chloride zinc plating intermediate（High temperature carrier）

High turbidity point: above 90 degrees, when the temperature is 10-55 degrees, the working liquid can produce normally.

High salt resistance: electroplating solution potassium chloride content up to 280g/L, no salting out.

High brightness: adapt to the secondary brightener benzylacetone or o-chlorobenzaldehyde, the combination of the two brightness is better.

Good coverage ability: good deep plating ability and even plating ability

Wide current range: 3A current in the 25 degree hull tank, the bath is not cloudy, no burning in the high area of the test piece. Electroplating users can open large current, shorten plating time, improve production efficiency, reduce comprehensive cost.

The preparation of potassium chloride zinc additive with HL-5 carrier has wide technological range, stable production and convenient maintenance.

Less decomposition, clear plating solution

20230920161435

New product acid zinc plating intermediate
It is a low foaming non ionic surfactant with a high cloud point.
Product Specification:
Chemical name
High temperature zinc plating carrier
Chemical content:
Polyethylene glycol mono(2-ethylhexyl) ether
CAS No.26468-86-0
Properties
Physical form: Colorless to pale yellow transparent liquid
pH: 5.0~7.0
Cloud point ≥45.0%
Water ≤20.0%
Content(%): ≥80.0%
Application
This is a low foaming non-ionic surfactant with a high cloud point. In acid zinc baths,it helps to solve the brightener and improves the deposition at high current density.
Packing
25kg/drum or 200kg/drum, stored in cool and dry place.